Detailed Product Description
Product Name: |
Mirror Aluminium |
Alloy: |
6063,6060,6463 |
|
|
|
Bright Dip |
Deep Process : |
Milling, Drilling ,Bending, Cutting |
Temper: |
T5,T6,T66 |
Heat Sink Polishing Surface Aluminum Extrusion Profile With Alloy 6463
Description:
1.Type:Aluminum profile
2.Model:Based on your drawings
3.Certificates:ISO9001
4.Production Ability:50,000 tons/year of aluminum profile
5.Usages: aluminum profile windows,doors,curtainwalls,etc.
6.Surface treatment:Anodize, natural
7.Production time:within 15-20 days
8. Usage: anodized aluminum profile for Industril aluminum profile
Material grade:Alloy:6063,6061,6005 aluminum profile
Order,payment,terms,shipment
1, Minimum order: 500kg per item and 1 ton per color, sample will be sent for customer free of charge provided by approval and kept for future mass production.
2, Sample Lead Time: working days(15 days for making the tool and 10 days making the samples. Before sending the samples to customer, samples should pass strict test in our lab. )Production Lead time: it depends on customers order quantity ( 30 working days after deposit).
3, Payment: 30% upon order confirmation and balance before delivery by T/T
4, Tooling:100% prepaid by T/T.
Primary Technical Data
1) Chemical composition
Alloy |
Si |
Mg |
Fe |
Cu |
Mn |
Zn |
Cr |
Ti |
6063 |
0.2~0.6 |
0.45~0.90 |
<0.35 |
<0.10 |
<0.10 |
<0.10 |
<0.10 |
<0.10 |
6060 |
0.3~0.6 |
0.35~0.60 |
0.1~0.3 |
~ |
<0.10 |
<0.15 |
<0.05 |
~ |
6463 |
0.2~0.6 |
0.45~0.90 |
<0.15 |
<0.20 |
<0.05 |
<0.05 |
~ |
~ |
6005 |
0.6~0.9 |
0.40~0.60 |
<0.35 |
<0.10 |
<0.10 |
<0.10 |
<0.10 |
<0.10 |
6061 |
0.4~0.8 |
0.80~1.2 |
<0.70 |
0.15~0.4 |
<0.15 |
<0.25 |
0.04~0.35 |
<0.15 |
6082 |
0.7~1.3 |
0.60~1.2 |
<0.50 |
<0.1 |
0.4~1.0 |
<0.20 |
<0.25 |
<0.10 |
6351 |
0.7~1.3 |
0.40~0.8 |
<0.50 |
<0.1 |
0.4~0.8 |
<0.20 |
~ |
<0.10 |
2) Mechanical property
Alloy |
Temper |
Tensile strength |
Yield strength |
Elongation |
6063 |
T5 |
≥ 160Mpa |
≥ 110Mpa |
≥ 8% |
T6 |
≥ 205Mpa |
≥ 180Mpa |
≥ 8% |
|
6061 |
T5 |
≥ 265Mpa |
≥ 245Mpa |
≥ 8% |