submerged-arc welding wire H08A, ER05-6
Material: Aluminum / Aluminum Alloy
Diameter: 2.0mm,2.5mm,3.2mm,4.0mm,5.0mm
Melting Point: Normal
Weight: 5~20kg/spool, 250~350kg/drum
Application: welding
Flux Content: standard
Solder wire: quality goods
Packaging Detail: 15kgs/roll/carton, 72cartons/pallet, 21-24metric tons/20ft container
Submerged Arc Welding Wires
1.Dia :2.0mm-15.0mm
2.packing:5Kg,15Kg,250kg,350kg
Application:
This series of welding wire is mainly applied to
Material: Copper / Copper Alloy
Diameter: 0.8mm-1.6mm
Melting Point: Normal
Weight:5~20kg/spool;250~350kg/drum
Flux Content: standard
solder wire: cheap price
Application: welding
Co2 welding wire AWS ER70S-6, 1.2mm
Material: Cooper plating
Wire Size: 0.8mm 1.0mm 1.2mm 1.6mm
HO8Mn2SiA Ho8Mn2Si Ho8Mn2SiMoa
Spool Size: D100mm, D200mm,D270mm,D300mm,K300mm
Melting Point 500(℃)
Net Weight: 1kg,5kg,15kg,18kg,20kg
Application: welding low carbon steel and high strength steel structure
GB/8110-1995 ISO9001:2000
Fast melting rate, high depositing efficiency, stable arc, little spatter, beautiful seam
1. Properties: Used for welding low carbon steel and low alloy steel structures, especially for welding of thin plates and can be applied to carbon steels, vehicles, construction, shipbuilding, bridge building, etc.
2. Product features: have excellent mechanical performance such as fast melting rate, high depositing efficiency, stable arc, little spatter, beautiful seam. Suitable for all-position welding work.
3. Technical data:
A. Chemical composition: C0.06-0.15, Mn 1.40-1.85, Si 0.80-1.15, P <=0.025, S <=0.035, Cu <=0.35, Ni <=0.30, Cr <=0.20
B. Tensile strength: ≥500MPa, yield point: ≥420MPa, elongation: ≥22, AK-V impact value: ≥27(-29)