Titanium is a new type of metal ,the performance of titanium is related to the content of carbon ,nitrogen ,hydrogen and oxygen .The pure titanium iodide impurity content less than 0.1%,but its low strength ,high performance plastic .99.5%pure titianium is :the density of (ρ)is 4.5g/cm3,the melting point of 172 silicon titanium alloy wear-resisting flooring 5℃，coefficient of heat conductivity is 15.24w/(m.k),tensile strength b is 539mpa ,elongation is 25%,section shrinkage of PSI is 25%,elastic modulus e is 1.078*105Mpa ,hardness hb195.
Titanium Characterisitic:high intensity ,hingh thermal strength ,good corrosion resistance ,good low temperature performance ,chemical active
Titanium alloy density is about 4.5g/cm3,only 60%of steel ,the strength of pure titanium was close to ordinary steel strength ,high strength titanium alloy than many alloy structural steel strength.Therefore titanium alloy strength (strength/density)is much larger than other metal structure materials ,see table ,can be produced the unit has high strength ,good rigigdity ,light quality zero components .The engine component,the plane frame ,skin ,fasteners and landing gear and so the use of titanium alloy.
The supply of titanium plate thickness:0.3mm-30mm;
Perennial supply grade :TA1,TA2,TC4
Cutting :cutting machine ,water cutting ,wire cutting ;
We solemnly promise :reliable quality ,henuine goods at a fair price .Titanium plate there are two kinds of performance standards:
GB/T3621-2007,GB/T13810-2007;B265 ASTM F136
American Standard is ASTM ,ASTM F67,AMS4928.
1、Grade:
American Standard garde:GR1,GR2,GR3,GR5,GR7,GR12
Russian Standard garde :TA0,TA2,TA3,TA5,TA6,TA7,TA9,TA10,TB2,TC1,TC2,TC3,TC4
Application standard：
1：GB228meatalic material tensile testing at ambient temperature.
2:GB/T3620.1titanium and titanium alloy and chemical composition
3:GB/T3620.2chemical components and components of titanium and titanium alloys are allowed to be misalighned.
4:GB4689chemical analysis method of titanium sponge ,titanium ferroalloy .
Titanium plate production specification:
T0.5-1.0mm×W1000mm×L2000-4000mm
T1.0-5.0mm×W1000-1500mm×L2000-3500mm
T5.0-30mm×W1000-2500mm×L3000-6000mm
T30-80mm×W1000mm×L2000mm
2、Titanium plate production status:
Hot working state(R) Cold working state (Y) Annealed condition (M)
3、Titanium plate manufacturing process；
Hot forging process in metal above the recrystallization temperature .
Hot rolled under the above the recrystallization temperature of the rolling process.
Cold plastic deformation temperature is lower than the temperature of the rolling process.
4、The characterisitic of titanium plate :
(1)Titanium plate surface oxide film is equivalent to a good durability with separting agent ,using titanium plate saves separating agent ,so the plate is easy to peel .eliminates the process of plate pretreatment ,titanium plate to light than copper plate .
(2)Half titanium plate is the titanium the life of a copper plate more than 3 times ,according to the operating conditions of up ti 10to 20years with .
(3)Compact rystal copper titanium plate making ,smooth surface ,good quality .
(4)Because of titanium plate without smearing separating agent ,which can aviod the pollution .
(5)Increase in copper electrolyte lower the production of electrolytic copper production costs ,which have good economic benefits.